If standard moulded single or double drainer sinktops are not suitable then we can fabricate sinktops to other sizes and configurations to suit your requirement. Using 15 mm thick sheet and combining it with various sinks from our standard range, drainer types (moulded drainers, drainer board or machined drainer grooves) and edgings or upstands we should be able to fabricate whatever sinktops you may need.
Please submit a drawing of the sinktop that you require and we will advise how close to that specification we are able to get.
The colours shown on this website are a guide only and cannot be guaranteed to match the colour of components supplied by Simmons.
(24 hour sport test. Based on BS EN 438-2:1991).
Acetone
Unaffected
Acetonitrile
Unaffected
Ammonium Hydroxide – 28%
Unaffected
Aqua regia
Unaffected
Benzyl alcohol
Unaffected
Chloroform
Unaffected
Chloroform – 100%
Unaffected
Chromic acid pickle (*1)
Unaffected
Dicholoromethane
Surface attack
Dimethylformamide
Unaffected
Ethyl acetate
Unaffected
Formaldehyde – 37%
Unaffected
Hydrochloric acid – 30%
Unaffected
Hydrochloric acid – concentrated
Unaffected
Hydrofluoric acid – 40%
Slight bleaching
Hydrogen Peroxide
Unaffected
Methanol
Unaffected
Nitric acid – 70%
Very slight bleaching
Nitric acid – concentrated
Slight yellowing
Nitric acid – fuming
Attack and staining
Perchloric acid – 0.1N
Unaffected
Phosphoric acid – concentrated
Unaffected
Potassium hydroxide pellet (*2)
Unaffected
Sodium hydroxide – 50%
Unaffected
Sodium hydroxide pellet (*2)
Unaffected
Sodium hypochlorite
Unaffected
Sulphuric acid – 70%
Unaffected
Sulphuric acid – concentrated
Surface attack
Xylene
Unaffected
Tensile strength
85 N/mm²
Tensile Modulus
10,500 N/mm²
Elongation at break
0.8%
Flexural strength
112 N/mm²
Flexural Modulus
10,000 N/mm²
Compressive strength
190 N/mm²
Coefficient of linear thermal expansion
34 x 10⁶
Water absorption – 24 hours at 23ºC
5–10 mg (0.06–0.068%) ISO 62 (1980)
Thermal Shock
2000 cycles (90 sec. at 75ºC, 90 sec. dwell, 90 sec. at 15ºC)
No effect
Should not be used with dry-ice or liquid nitrogen
Smoke Emission
Low Smoke Emission – BS 6853 1999 App. D Clause d.8.4
Result – Ao(on) 8.75, Ao(off) 10.41
Flammability
Class 0
Thermal Decomposition
350ºC
Glass transition temperature (Tg)
120 – 130ºC
Decontamination factor (geometric mean)
5598.0
Deviation factor
1.25
Ease of radioactive decontamination classification
"Excellent"
As with all worktops a reasonable standard of laboratory housekeeping will help to keep the worktops in good condition. All spillages should be cleaned up as soon as possible. Staining agents and aggressive chemicals should not be allowed to sit in contact with the tops for a prolonged period of time.
Areas of chemical attack or staining can be removed with a polishing compound or very fine abrasive paper, but it should be stressed that this will alter the finish of the surface. Performance will not be affected.
The use of a wax furniture polish will help to retain the gloss finish.
Components should not be exposed to dry-ice or liquid nitrogen and heat insulation pads should be placed between a top and a steambath or hotplate to prevent thermal stress.
Sinks can be supplied complete with a chemically resistant polypropylene waste in grey, white or black is required. Wastes have a 73mm diameter flange and a 1½ inch BSP tail and will connect to the relevant Vulcathene industrial waste components. These can also be combined with a standing waste tube or an overflow kit.